The microstructural effect of low-dose neutron irradiation and subsequent high-temperature tempering in the reduced activation ferritic/martensitic steel F82H-mod. (7.73 Cr, 0.09 C, 0.08 Mn, 0.19 V, 2.06 W, 0.02 Ta, wt%, bal. Fe) has been studied using small-angle neutron scattering (SANS). The investigated samples were irradiated with thermal neutrons at 523 K, to dose levels of 2.4 displacements per atom then tempered for 2 h at 1043 K. The SANS measurements were carried out at the D22 instrument of the High Flux Reactor at the Institut Max von Laue-Paul Langevin, Grenoble, France. The differences observed in nuclear and magnetic small-angle neutron scattering cross-sections after subtraction of the reference sample from the irradiated one suggest that the irradiation and the subsequent post-irradiation tempering produce the growth of non-magnetic precipitates; the results are also compared with those obtained on other ferritic/martensitic steels, with different chemical composition, irradiated under the same conditions.

Microstructural investigation of low-dose neutron irradiation effects in martensitic steels for nuclear application by means of small-angle neutron scattering

Valli, M.
2007-04-01

Abstract

The microstructural effect of low-dose neutron irradiation and subsequent high-temperature tempering in the reduced activation ferritic/martensitic steel F82H-mod. (7.73 Cr, 0.09 C, 0.08 Mn, 0.19 V, 2.06 W, 0.02 Ta, wt%, bal. Fe) has been studied using small-angle neutron scattering (SANS). The investigated samples were irradiated with thermal neutrons at 523 K, to dose levels of 2.4 displacements per atom then tempered for 2 h at 1043 K. The SANS measurements were carried out at the D22 instrument of the High Flux Reactor at the Institut Max von Laue-Paul Langevin, Grenoble, France. The differences observed in nuclear and magnetic small-angle neutron scattering cross-sections after subtraction of the reference sample from the irradiated one suggest that the irradiation and the subsequent post-irradiation tempering produce the growth of non-magnetic precipitates; the results are also compared with those obtained on other ferritic/martensitic steels, with different chemical composition, irradiated under the same conditions.
1-apr-2007
Tecnologie e metodologie diagnostiche
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/1211
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
social impact