An innovative diamond detector layout is presented that is designed to operate at high temperature under intense neutron and gamma fluxes. It is made of a 500 μm "electronic grade" diamond film with 100 nm thick Ag metal contacts deposited onto each surface of the film by means of thermal evaporation. A 2μm thick layer of 6LiF has been deposited on top of one of the two Ag contacts to make the detector sensitive to thermal neutrons. The device was tested at the ISIS spallation neutron source (Rutherford Appleton Laboratory, UK) using the INES beam line. The detector was continuously irradiated for 100 hours in vacuum (p = 10-5 mbar), exposed to a neutron flux of about 106 n cm-2 s-1 at a temperature T = 150°C. The aim of this experiment was to study the time dependence of the diamond detector performance while operating at high temperature under irradiation, providing a first experimental proof of reliable continuous operation for 100 hours at high temperature in a harsh environment. Copyright © EPLA, 2016.
High-temperature long-lasting stability assessment of a single-crystal diamond detector under high-flux neutron irradiation
Pietropaolo, A.;Vincenti, M.A.;Montereali, R.M.;Angelone, M.
2016-01-01
Abstract
An innovative diamond detector layout is presented that is designed to operate at high temperature under intense neutron and gamma fluxes. It is made of a 500 μm "electronic grade" diamond film with 100 nm thick Ag metal contacts deposited onto each surface of the film by means of thermal evaporation. A 2μm thick layer of 6LiF has been deposited on top of one of the two Ag contacts to make the detector sensitive to thermal neutrons. The device was tested at the ISIS spallation neutron source (Rutherford Appleton Laboratory, UK) using the INES beam line. The detector was continuously irradiated for 100 hours in vacuum (p = 10-5 mbar), exposed to a neutron flux of about 106 n cm-2 s-1 at a temperature T = 150°C. The aim of this experiment was to study the time dependence of the diamond detector performance while operating at high temperature under irradiation, providing a first experimental proof of reliable continuous operation for 100 hours at high temperature in a harsh environment. Copyright © EPLA, 2016.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.