The micro-structural effects of different neutron irradiation temperatures and helium contents, for 16 dpa dose, have been investigated by means of small-angle neutron scattering (SANS) in B-alloyed ferritic/martensitic steel Eurofer97-1 (0.12 C, 9 Cr, 0.2 V, 1.08 W wt%, B concentrations up to 1000 ppm); due to B transmutations, fusion relevant He/dpa values are expected to be produced under neutron irradiation. SANS measurements have been carried out on a sample irradiated at 350 °C, with estimated helium content of 5600 appm, and compared to previous SANS results, obtained on two other irradiated samples of this same B-alloyed steel. These new measurements confirm that for such high helium contents the SANS cross-section increases in order of magnitude and the magnetic SANS component is strongly reduced, compared to lower helium content (400 appm). Such effects are attributed to increase in helium bubbles density and to the presence of micro-cavities, produced after dissolution of large B-carbides. The SANS data analysis procedure has been improved, also thanks to the additional information provided by the new measurements, and more accurate helium bubble size distributions have been obtained for all the investigated samples. For 5600 appm helium content, bubble volume fractions are found of 0.025 for the sample irradiated at 350 °C and of 0.041 for the previously investigated sample irradiated at 400 °C, significantly increasing with the irradiation temperature. These values are approximately one order of magnitude larger than the value of 0.003 previously found for the sample with 400 appm helium. The size distributions are compared with electron microscopy observations of these same samples. It appears that the occurrence of complex micro-structural changes in irradiated Eurofer97-1 steel should be taken in due account when considering its application under high He/dpa ratio values. © 2018
Micro-structural effects of irradiation temperature and helium content in neutron irradiated B-alloyed Eurofer97-1 steel
Valli, M.;Coppola, R.
2018-01-01
Abstract
The micro-structural effects of different neutron irradiation temperatures and helium contents, for 16 dpa dose, have been investigated by means of small-angle neutron scattering (SANS) in B-alloyed ferritic/martensitic steel Eurofer97-1 (0.12 C, 9 Cr, 0.2 V, 1.08 W wt%, B concentrations up to 1000 ppm); due to B transmutations, fusion relevant He/dpa values are expected to be produced under neutron irradiation. SANS measurements have been carried out on a sample irradiated at 350 °C, with estimated helium content of 5600 appm, and compared to previous SANS results, obtained on two other irradiated samples of this same B-alloyed steel. These new measurements confirm that for such high helium contents the SANS cross-section increases in order of magnitude and the magnetic SANS component is strongly reduced, compared to lower helium content (400 appm). Such effects are attributed to increase in helium bubbles density and to the presence of micro-cavities, produced after dissolution of large B-carbides. The SANS data analysis procedure has been improved, also thanks to the additional information provided by the new measurements, and more accurate helium bubble size distributions have been obtained for all the investigated samples. For 5600 appm helium content, bubble volume fractions are found of 0.025 for the sample irradiated at 350 °C and of 0.041 for the previously investigated sample irradiated at 400 °C, significantly increasing with the irradiation temperature. These values are approximately one order of magnitude larger than the value of 0.003 previously found for the sample with 400 appm helium. The size distributions are compared with electron microscopy observations of these same samples. It appears that the occurrence of complex micro-structural changes in irradiated Eurofer97-1 steel should be taken in due account when considering its application under high He/dpa ratio values. © 2018I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.