Electron beam (EB) welding has been used to realize the seams on 2 mm thick plates of directionally solidified (DS) IN792 superalloy. A grid of the samples has been prepared by varying the pass speed v from 1 to 2.5 m/min, while the other process parameters (power P = 1 kW, acceleration voltage T = 50 kV, beam current I = 20 mA) were kept constant. Experiments were carried out both at room temperature and with pre-heating at 200 °C or 300 °C. Once found the best process conditions (pre-heating at 300 °C; v = 2.5 m/min) the effect of postwelding heat treatments at 700 and 750 °C for increasing time up to 2 hours has been investigated. © 2017 Trans Tech Publications, Switzerland.

IN792 DS superalloy: Optimization of EB welding and post-welding heat treatments

Barbieri, G.
2017-01-01

Abstract

Electron beam (EB) welding has been used to realize the seams on 2 mm thick plates of directionally solidified (DS) IN792 superalloy. A grid of the samples has been prepared by varying the pass speed v from 1 to 2.5 m/min, while the other process parameters (power P = 1 kW, acceleration voltage T = 50 kV, beam current I = 20 mA) were kept constant. Experiments were carried out both at room temperature and with pre-heating at 200 °C or 300 °C. Once found the best process conditions (pre-heating at 300 °C; v = 2.5 m/min) the effect of postwelding heat treatments at 700 and 750 °C for increasing time up to 2 hours has been investigated. © 2017 Trans Tech Publications, Switzerland.
2017
9783035711295
Welding;Electron beam;Superalloys;Post-welding treatments;Microstructure
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/4460
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
social impact