Planar perovskite solar cells and modules were realized by using low temperature solution-process fabrication procedures. The photovoltaic performance was improved by optimizing a SnO2 electron transport layer and its interface with the perovskite layer. We achieved a power conversion efficiency (PCE) of 17.3% on small area cell (0.09 cm2) with negligible hysteresis and a steady-state PCE equal to 17.4%. Furthermore, shelf life tests showed a relative decrease of only 5% in PCE from its initial value after 1000 h of storage in dark conditions in air (RH 20%). Up-scaling of the technology was implemented entirely in air with fabrication of modules with a high aperture ratio of 91%. The modules delivered a maximum PCE of 13.1% obtained on an active area of 13.8 cm2 and of 11.9% on an aperture area of 15.2 cm2 representing state of art performance for fully low temperature solution processed planar perovskite solar modules.

Low temperature, solution-processed perovskite solar cells and modules with an aperture area efficiency of 11%

Palma A. L.;
2018-01-01

Abstract

Planar perovskite solar cells and modules were realized by using low temperature solution-process fabrication procedures. The photovoltaic performance was improved by optimizing a SnO2 electron transport layer and its interface with the perovskite layer. We achieved a power conversion efficiency (PCE) of 17.3% on small area cell (0.09 cm2) with negligible hysteresis and a steady-state PCE equal to 17.4%. Furthermore, shelf life tests showed a relative decrease of only 5% in PCE from its initial value after 1000 h of storage in dark conditions in air (RH 20%). Up-scaling of the technology was implemented entirely in air with fabrication of modules with a high aperture ratio of 91%. The modules delivered a maximum PCE of 13.1% obtained on an active area of 13.8 cm2 and of 11.9% on an aperture area of 15.2 cm2 representing state of art performance for fully low temperature solution processed planar perovskite solar modules.
2018
Low temperature, Perovskite solar cell, Photovoltaic modules, Planar, SnO; 2, Solution-process
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/52422
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 51
social impact