Pulsed laser deposited thin Y Ba2Cu3O7-x (YBCO) films with pinning additions of 5 at. % Ba2Y TaO6 (BYTO) were compared to films with 2.5 at. % Ba2Y TaO6 + 2.5 at. % Ba2Y NbO6 (BYNTO) additions. Excellent magnetic flux-pinning at 77 K was obtained with remarkably high irreversibility fields greater than 10 T (YBCO-BYTO) and 11 T (YBCO-BYNTO), representing the highest ever achieved values in YBCO films. © 2016 Author(s).

Enhanced 77 K vortex-pinning in y Ba2Cu3O7-x films with Ba2Y TaO6 and mixed Ba2Y TaO6 + Ba2Y NbO6 nano-columnar inclusions with irreversibility field to 11 T

Vannozzi, A.;Rufoloni, A.;Pinto, V.;Mancini, A.;Galluzzi, V.;Angrisani Armenio, A.;Augieri, A.;Rizzo, F.;Celentano, G.
2016

Abstract

Pulsed laser deposited thin Y Ba2Cu3O7-x (YBCO) films with pinning additions of 5 at. % Ba2Y TaO6 (BYTO) were compared to films with 2.5 at. % Ba2Y TaO6 + 2.5 at. % Ba2Y NbO6 (BYNTO) additions. Excellent magnetic flux-pinning at 77 K was obtained with remarkably high irreversibility fields greater than 10 T (YBCO-BYTO) and 11 T (YBCO-BYNTO), representing the highest ever achieved values in YBCO films. © 2016 Author(s).
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/1400
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
social impact