The wear and fretting behaviour of IN625 cold spray coatings was analysed and the results are presented. The cold spray conditions were selected in order to obtain coatings with minimum porosity and maximum particles splat. This leads to compact and hard deposited material able to resist wear damaging and to dissipate energy during fretting. The coating’s strength was evaluated through nanoindentation that revealed an increased hardness from the surface toward the substrate. This different hardening behaviour from the coating surface toward the substrate leads to increased resistance to fretting and wear as the maximum stresses increase. This was revealed by scratch tests performed at linearly increasing loads that allowed identifying of the damage mechanisms acting on the coating as the triaxial stresses increase. The hardening behaviour of the coating also influ-enced the fretting behaviour revealed by the weight loss experienced by varying the fretting maximum load. © 2020 by the authors.

Wear and Fretting Behavior of Cold Sprayed IN625 Superalloy

Antonella Rizzo;Daniele Valerini;Laura Capodieci
2020-01-01

Abstract

The wear and fretting behaviour of IN625 cold spray coatings was analysed and the results are presented. The cold spray conditions were selected in order to obtain coatings with minimum porosity and maximum particles splat. This leads to compact and hard deposited material able to resist wear damaging and to dissipate energy during fretting. The coating’s strength was evaluated through nanoindentation that revealed an increased hardness from the surface toward the substrate. This different hardening behaviour from the coating surface toward the substrate leads to increased resistance to fretting and wear as the maximum stresses increase. This was revealed by scratch tests performed at linearly increasing loads that allowed identifying of the damage mechanisms acting on the coating as the triaxial stresses increase. The hardening behaviour of the coating also influ-enced the fretting behaviour revealed by the weight loss experienced by varying the fretting maximum load. © 2020 by the authors.
2020
Cold spray
Fretting
Nanoindentation
Scratch
Wear
File in questo prodotto:
File Dimensione Formato  
Wear and Fretting Behavior of Cold Sprayed IN625 Superalloy.pdf

accesso aperto

Tipologia: Versione Editoriale (PDF)
Licenza: Creative commons
Dimensione 7 MB
Formato Adobe PDF
7 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/66269
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 7
social impact