Activated hard carbons, obtained from the pyrolysis of various waste biomasses, were prepared and characterized for use as the active material for the fabrication of battery electrodes. The preparation consisted of a pyrolysis process, followed by an activation with KOH and a further high-temperature thermal process. TG and DTA were used to discriminate the steps of the activation process, while SEM, XRD, and Raman characterization were employed to evaluate the effects of activation. The activated carbons were tested as electrodes in lithium-sulfur and lithium-ion batter-ies. The carbonaceous materials coming from cherry stones and walnut shells have proved to be particularly suitable as electrode components. When used as anodes in lithium-ion batteries, both carbons exhibited a high first cycle discharge capacity, which was not restored during the next charge. After the first two cycles, in which there was a marked loss of capacity, both electrodes showed good reversibility. When used as cathodes in lithium-sulfur batteries, both carbons exhibited good catalytic activity against the redox reaction involving sulfur species with good cycle stability and satisfactory Coulombic efficiency.

Hard Carbons for Use as Electrodes in Li-S and Li-ion Batteries

Pozio A.;Di Carli M.;Aurora A.;Falconieri M.;Della Seta L.;Prosini P. P.
2022-01-01

Abstract

Activated hard carbons, obtained from the pyrolysis of various waste biomasses, were prepared and characterized for use as the active material for the fabrication of battery electrodes. The preparation consisted of a pyrolysis process, followed by an activation with KOH and a further high-temperature thermal process. TG and DTA were used to discriminate the steps of the activation process, while SEM, XRD, and Raman characterization were employed to evaluate the effects of activation. The activated carbons were tested as electrodes in lithium-sulfur and lithium-ion batter-ies. The carbonaceous materials coming from cherry stones and walnut shells have proved to be particularly suitable as electrode components. When used as anodes in lithium-ion batteries, both carbons exhibited a high first cycle discharge capacity, which was not restored during the next charge. After the first two cycles, in which there was a marked loss of capacity, both electrodes showed good reversibility. When used as cathodes in lithium-sulfur batteries, both carbons exhibited good catalytic activity against the redox reaction involving sulfur species with good cycle stability and satisfactory Coulombic efficiency.
2022
activated carbon
Li-ion battery
Li-sulfur battery
pyrolysis
waste biomass
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/70627
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 12
social impact