Glass-fiber reinforced thermosetting plastic adhesive joints were characterized through ultrasonic imaging and lock-in thermographic analysis for assessing the adhesion quality before being subjected to static tensile mechanical tests and to accelerated aging cycles. The mapping of each sample has been obtained. Visual testing were performed on all specimens after the mechanical tests in order to obtain a comparison with ultrasonic and lock-in thermography technique. A quantitative analysis has been carried out to evaluate the ability of lock-in thermography in investigating inadequate bonding and obtaining the validation of the technique by the consistency of the results with the well-established ultrasonic testing. © 2015 Published by Elsevier Ltd.

Ultrasonic analysis and lock-in thermography for debonding evaluation of composite adhesive joints

Luprano V.A.M.;Aversa P.;
2016-01-01

Abstract

Glass-fiber reinforced thermosetting plastic adhesive joints were characterized through ultrasonic imaging and lock-in thermographic analysis for assessing the adhesion quality before being subjected to static tensile mechanical tests and to accelerated aging cycles. The mapping of each sample has been obtained. Visual testing were performed on all specimens after the mechanical tests in order to obtain a comparison with ultrasonic and lock-in thermography technique. A quantitative analysis has been carried out to evaluate the ability of lock-in thermography in investigating inadequate bonding and obtaining the validation of the technique by the consistency of the results with the well-established ultrasonic testing. © 2015 Published by Elsevier Ltd.
2016
Glass-fiber reinforced plastic (GFRP);Ultrasonic C-scan;Adhesive joints;Lock-in thermography
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12079/819
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
social impact